Descripción del título
Alternativas para mejorar l...
With the aim to improve the resistance to the waste of teeth of PMMA used in total prosthesis, in the preliminary stage different alternatives of reinforcement materials were evaluated as hydroxyapatite, ceramic spheres and Wollastonita. Once selected the Wollastonita, we defined an appropriate relationship monomer ~ polymer and a silane like couple agent. On the elaborated samples following a standard industrial procedure, they were carried out qualitative and quantitative tests to evaluate the quality of the PMMA reinforced regarding the PMMA without commonly used reinforcement. From the resistance tests to the waste and hardness it is observed that the addition of the Wollastonite produces an improvement in this properties, although for the resistance test to the indentation, in some cases a deterioration is presented regarding the value settled down in the norm ICONTEC 159 I defined to evaluate the behavior of teeth manufactured starting from synthetic resins. The results indicate a special sensibility to the homogenization of the mixture PMMA-Wollastonite and the necessity of a pre~ treatment of the Wollastonite with the silane g~aminopropiltrietoxisilane to improve the compatibility between this and the PMMA. Compound materials were obtained very conformed from the point of view of the union of the phases that compose it, without producing significant changes in processes involved in the production of such dental pieces as preparation and pressed. They are necessary some adjustments before their possible application to industrial scale, among those that stand out, to obtain a better dispersion of tl1e Wollasto¬nite to avoid tl1e agglomerates tl1at add some betas to tl1e final product and a new formulation of tl1e colorings to adjust tl1e color to tl1e traditionally used guides
Con el objetivo de mejorar la resistencia al desgaste de dientes de PMMA utilizados en prótesis total. En la etapa preliminar se evaluaron diferentes alternativas de materiales de refuerzo como hidroxiapatita. esferas cerámicas y Wollastonita. Una vez seleccionada la Wollastonita se definieron una adecuada relación monómero - polímero y un silano como agente de acople. Sobre las muestras elaboradas siguiendo un procedimiento industrial estándar. Se realizaron pruebas cualitativas y cuantitativas para evaluar la calidad del PMMA reforzado respecto al PMMA sin refuerzo comúnmente utilizado. De las pruebas de resistencia al desgaste 'y de dureza se observa que la adición de la Wollastonita produce una mejora en dichas propiedades. aunque para la prueba de resistencia a la indentación. en algunos casos se presenta una desmejora respecto al valor establecido en la norma ICONTEC 1591 para evaluar el comportamiento de dientes fabricados a partir de resinas sintéticas. Los resultados indican una especial sensibilidad a la homogenización de la mezcla PMMA-Wollastonita y la necesidad de un pretratamiento de la Wollastonita con el silano g~aminopropiltrietoxisilano para mejorar la compatibilidad entre ésta y el PMMA. Se obtuvieron materiales compuestos bien conformados desde el punto de vista de la unión de las fases que lo componen. sin producir cambios significativos en procesos involucrados en la fabricación de piezas dentales tales como preparación y prensado. Son necesarios algunos ajustes antes de su posible aplicación a escala industrial. entre los que se destacan, obtener una mejor dispersión de la Wollastonita para evitar los aglomerados que adicionan algunas betas al producto final y una nueva formulación de los colorantes para ajustar el color a las guías tradicionalmente usadas
Analítica
analitica Rebiun32948033 https://catalogo.rebiun.org/rebiun/record/Rebiun32948033 230421s2002 xx o 000 0 spa d https://dialnet.unirioja.es/servlet/oaiart?codigo=4804632 (Revista) ISSN 0120-8705 S9M oai:dialnet.unirioja.es:ART0000682991 https://dialnet.unirioja.es/oai/OAIHandler 14 DGCNT S9M S9M dc Alternativas para mejorar las propiedades mecánicas de dientes de PMMA utilizados en prótesis total - estudio de viabilidad electronic resource] 2002 application/pdf Open access content. Open access content star With the aim to improve the resistance to the waste of teeth of PMMA used in total prosthesis, in the preliminary stage different alternatives of reinforcement materials were evaluated as hydroxyapatite, ceramic spheres and Wollastonita. Once selected the Wollastonita, we defined an appropriate relationship monomer ~ polymer and a silane like couple agent. On the elaborated samples following a standard industrial procedure, they were carried out qualitative and quantitative tests to evaluate the quality of the PMMA reinforced regarding the PMMA without commonly used reinforcement. From the resistance tests to the waste and hardness it is observed that the addition of the Wollastonite produces an improvement in this properties, although for the resistance test to the indentation, in some cases a deterioration is presented regarding the value settled down in the norm ICONTEC 159 I defined to evaluate the behavior of teeth manufactured starting from synthetic resins. The results indicate a special sensibility to the homogenization of the mixture PMMA-Wollastonite and the necessity of a pre~ treatment of the Wollastonite with the silane g~aminopropiltrietoxisilane to improve the compatibility between this and the PMMA. Compound materials were obtained very conformed from the point of view of the union of the phases that compose it, without producing significant changes in processes involved in the production of such dental pieces as preparation and pressed. They are necessary some adjustments before their possible application to industrial scale, among those that stand out, to obtain a better dispersion of tl1e Wollasto¬nite to avoid tl1e agglomerates tl1at add some betas to tl1e final product and a new formulation of tl1e colorings to adjust tl1e color to tl1e traditionally used guides Con el objetivo de mejorar la resistencia al desgaste de dientes de PMMA utilizados en prótesis total. En la etapa preliminar se evaluaron diferentes alternativas de materiales de refuerzo como hidroxiapatita. esferas cerámicas y Wollastonita. Una vez seleccionada la Wollastonita se definieron una adecuada relación monómero - polímero y un silano como agente de acople. Sobre las muestras elaboradas siguiendo un procedimiento industrial estándar. Se realizaron pruebas cualitativas y cuantitativas para evaluar la calidad del PMMA reforzado respecto al PMMA sin refuerzo comúnmente utilizado. De las pruebas de resistencia al desgaste 'y de dureza se observa que la adición de la Wollastonita produce una mejora en dichas propiedades. aunque para la prueba de resistencia a la indentación. en algunos casos se presenta una desmejora respecto al valor establecido en la norma ICONTEC 1591 para evaluar el comportamiento de dientes fabricados a partir de resinas sintéticas. Los resultados indican una especial sensibilidad a la homogenización de la mezcla PMMA-Wollastonita y la necesidad de un pretratamiento de la Wollastonita con el silano g~aminopropiltrietoxisilano para mejorar la compatibilidad entre ésta y el PMMA. Se obtuvieron materiales compuestos bien conformados desde el punto de vista de la unión de las fases que lo componen. sin producir cambios significativos en procesos involucrados en la fabricación de piezas dentales tales como preparación y prensado. Son necesarios algunos ajustes antes de su posible aplicación a escala industrial. entre los que se destacan, obtener una mejor dispersión de la Wollastonita para evitar los aglomerados que adicionan algunas betas al producto final y una nueva formulación de los colorantes para ajustar el color a las guías tradicionalmente usadas LICENCIA DE USO: Los documentos a texto completo incluidos en Dialnet son de acceso libre y propiedad de sus autores y/o editores. Por tanto, cualquier acto de reproducción, distribución, comunicación pública y/o transformación total o parcial requiere el consentimiento expreso y escrito de aquéllos. Cualquier enlace al texto completo de estos documentos deberá hacerse a través de la URL oficial de éstos en Dialnet. Más información: https://dialnet.unirioja.es/info/derechosOAI | INTELLECTUAL PROPERTY RIGHTS STATEMENT: Full text documents hosted by Dialnet are protected by copyright and/or related rights. This digital object is accessible without charge, but its use is subject to the licensing conditions set by its authors or editors. Unless expressly stated otherwise in the licensing conditions, you are free to linking, browsing, printing and making a copy for your own personal purposes. All other acts of reproduction and communication to the public are subject to the licensing conditions expressed by editors and authors and require consent from them. Any link to this document should be made using its official URL in Dialnet. More info: https://dialnet.unirioja.es/info/derechosOAI Spanish PMMA Refuerzo Wollastonita Resistencia al desgaste Wollastonite Resistance to the waste text (article) Álvarez L., Mónica Lucía. cre García, Lina M. cre Restrepo R., Ramiro. cre Abad M., Pablo. cre Peláez Vargas, Alejandro. cre Revista CES Medicina, ISSN 0120-8705, Vol. 16, Nº. 2, 2002, pags. 43-48 Revista CES Medicina, ISSN 0120-8705, Vol. 16, Nº. 2, 2002, pags. 43-48 Revista CES Medicina, ISSN 0120-8705, Vol. 16, Nº. 2, 2002, pags. 43-48