Descripción del título
Aggregate particle size int...
The size distribution, the gradation and the type of aggregates are factors of great relevance for the design of mixtures in concrete and construction materials in general since these allow us to obtain information on the voids contents, module fineness, bulk density, and mechanical performance that certain aggregate mixtures will present. In the present work, different mixtures of aggregates were made using three types of raw materials: fine sand, coarse sand, and 3/8" aggregate, for which their mineralogical composition was evaluated using X-ray diffraction, the chemical composition using X-ray fluorescence, and its macroscopic structure using optical microscopy. Sixty-six mixture formulations were made, to which variables such as fineness modulus, particle size distribution, void content, and density were evaluated. These data were represented in ternary diagrams. From the gradation studies carried out, six formulations were selected based on the type of aggregate used and the content of voids. With this selection, concrete specimens were made, which were subjected to compression tests, finding that the mixture A 22, with 17 % of voids generated a compressive strength of 22 MPa. The results obtained can be used not only in applications such as zero-set concrete, concrete block masonry, or regular concretes, but also in asphalt pavements, ceramic materials obtained by sintering, and particle-reinforced composite materials
La distribución de tamaño, las interrelaciones de gradación y el tipo de agregados, son factores de gran relevancia para el diseño de mezclas en concretos y en materiales de construcción en general, debido a que estos nos permiten obtener información sobre el porcentaje de vacíos, módulo de finura, densidad aparente y el rendimiento mecánico que presentarán determinadas mezclas de agregados. En el presente trabajo se realizaron diferentes mezclas de agregados utilizando tres tipos de materias primas con diferentes granulometrías: arena fina, arena gruesa y agregado de 3/8", para las cuales se evaluó su composición mineralógica mediante difracción de rayos X, la composición química empleando fluorescencia de rayos X, y su estructura macroscópica mediante microscopía óptica. Se realizaron 66 mezclas, a las cuales se les evaluaron variables como módulo de finura, distribución de tamaño de partícula, contenido de vacíos y densidad. Estos datos se representaron en diagramas ternarios. De los estudios de gradación realizados, se seleccionaron seis formulaciones en función del tipo de agregado utilizado y el contenido de vacíos. Con esta selección, se realizaron probetas de concreto, las cuales fueron sometidas a pruebas de compresión, encontrando que por ejemplo para la mezcla A 22 que con un porcentaje de vacíos de 17 % generó una resistencia a la compresión de 22 MPa. Los resultados obtenidos se pueden usar no solo en aplicaciones tales como concretos con cero asentamiento, mampostería de bloques de hormigón o en los hormigones regulares, sino además en pavimentos asfálticos, materiales cerámicos obtenidos por sinterizado, y materiales compuestos reforzados con partículas
Analítica
analitica Rebiun33842488 https://catalogo.rebiun.org/rebiun/record/Rebiun33842488 230421s2020 xx o 000 0 eng d https://dialnet.unirioja.es/servlet/oaiart?codigo=7590765 (Revista) ISSN 0122-056X (Revista) ISSN 2256-5035 S9M oai:dialnet.unirioja.es:ART0001411277 https://dialnet.unirioja.es/oai/OAIHandler 16 DGCNT S9M S9M dc Aggregate particle size interrelations and case study in concrete using white ordinary Portland cement electronic resource] 2020 application/pdf Open access content. Open access content star The size distribution, the gradation and the type of aggregates are factors of great relevance for the design of mixtures in concrete and construction materials in general since these allow us to obtain information on the voids contents, module fineness, bulk density, and mechanical performance that certain aggregate mixtures will present. In the present work, different mixtures of aggregates were made using three types of raw materials: fine sand, coarse sand, and 3/8" aggregate, for which their mineralogical composition was evaluated using X-ray diffraction, the chemical composition using X-ray fluorescence, and its macroscopic structure using optical microscopy. Sixty-six mixture formulations were made, to which variables such as fineness modulus, particle size distribution, void content, and density were evaluated. These data were represented in ternary diagrams. From the gradation studies carried out, six formulations were selected based on the type of aggregate used and the content of voids. With this selection, concrete specimens were made, which were subjected to compression tests, finding that the mixture A 22, with 17 % of voids generated a compressive strength of 22 MPa. The results obtained can be used not only in applications such as zero-set concrete, concrete block masonry, or regular concretes, but also in asphalt pavements, ceramic materials obtained by sintering, and particle-reinforced composite materials La distribución de tamaño, las interrelaciones de gradación y el tipo de agregados, son factores de gran relevancia para el diseño de mezclas en concretos y en materiales de construcción en general, debido a que estos nos permiten obtener información sobre el porcentaje de vacíos, módulo de finura, densidad aparente y el rendimiento mecánico que presentarán determinadas mezclas de agregados. En el presente trabajo se realizaron diferentes mezclas de agregados utilizando tres tipos de materias primas con diferentes granulometrías: arena fina, arena gruesa y agregado de 3/8", para las cuales se evaluó su composición mineralógica mediante difracción de rayos X, la composición química empleando fluorescencia de rayos X, y su estructura macroscópica mediante microscopía óptica. Se realizaron 66 mezclas, a las cuales se les evaluaron variables como módulo de finura, distribución de tamaño de partícula, contenido de vacíos y densidad. Estos datos se representaron en diagramas ternarios. De los estudios de gradación realizados, se seleccionaron seis formulaciones en función del tipo de agregado utilizado y el contenido de vacíos. Con esta selección, se realizaron probetas de concreto, las cuales fueron sometidas a pruebas de compresión, encontrando que por ejemplo para la mezcla A 22 que con un porcentaje de vacíos de 17 % generó una resistencia a la compresión de 22 MPa. Los resultados obtenidos se pueden usar no solo en aplicaciones tales como concretos con cero asentamiento, mampostería de bloques de hormigón o en los hormigones regulares, sino además en pavimentos asfálticos, materiales cerámicos obtenidos por sinterizado, y materiales compuestos reforzados con partículas LICENCIA DE USO: Los documentos a texto completo incluidos en Dialnet son de acceso libre y propiedad de sus autores y/o editores. Por tanto, cualquier acto de reproducción, distribución, comunicación pública y/o transformación total o parcial requiere el consentimiento expreso y escrito de aquéllos. Cualquier enlace al texto completo de estos documentos deberá hacerse a través de la URL oficial de éstos en Dialnet. Más información: https://dialnet.unirioja.es/info/derechosOAI | INTELLECTUAL PROPERTY RIGHTS STATEMENT: Full text documents hosted by Dialnet are protected by copyright and/or related rights. This digital object is accessible without charge, but its use is subject to the licensing conditions set by its authors or editors. Unless expressly stated otherwise in the licensing conditions, you are free to linking, browsing, printing and making a copy for your own personal purposes. All other acts of reproduction and communication to the public are subject to the licensing conditions expressed by editors and authors and require consent from them. Any link to this document should be made using its official URL in Dialnet. More info: https://dialnet.unirioja.es/info/derechosOAI English particulate reinforced composites aggregates size distribution gradation particle packing Portland cement particulate reinforced composites aggregates size distribution gradation particle packing Portland cement text (article) Colorado Lopera, Henry. cre Vélez, Juan Manuel. cre Castañeda Montoya, Manuela. cre Informador técnico, ISSN 2256-5035, Vol. 84, Nº. 2 (Julio-Diciembre), 2020, pags. 114-132 Informador técnico, ISSN 2256-5035, Vol. 84, Nº. 2 (Julio-Diciembre), 2020, pags. 114-132 Informador técnico, ISSN 2256-5035, Vol. 84, Nº. 2 (Julio-Diciembre), 2020, pags. 114-132