Descripción del título
Behavior of aluminum coatin...
Aluminum coatings have been obtained using the Chemical Vapor Deposition of Fluidized Bed Reactor technique (CVD-FBR), on austenitic stainless steels (AISI 304, AISI 316 and AISI 317), in order to evaluate resistance to steam oxidation at 700ºC. The coatings were characterized in their morphology/composition and crystalline phases using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Analysis (EDAX) and X-ray Diffraction (XRD). In addition, thermodynamic simulation was performed using Thermo-Calc software to make the deposition of the coating on said steels similar to optimal conditions. All specimens -with and without aluminum coating by CVD-FBR- were oxidized at 700ºC, in a steam atmosphere of nearly 100% for 1000 h. The aluminum coating prevented the formation of oxide islands or crust, and reduced steel mass gain. Coated AISI steel showed a 25% reduction in mass gain compared to the same steel uncoated and oxidized under the same conditions. AISI 316 and AISI 317 steels underwent loss of mass because the brittle oxide that was formed came loose
Foram obtidos recobrimentos de alumínio pela técnica de deposição química de vapor por leito fluidizado (CVD-FBR por suas siglas em inglês), sobre aços inoxidáveis austeníticos (AISI 304, AISI 316 e AISI 317), com o propósito de avaliar a resistência à oxidação em vapor d'água a 700ºC. Os recobrimentos foram caracterizados em sua morfologia/composição e fases cristalinas mediante as técnicas de Microscopia Eletrônica de Varredura (MEB), com análise de raios X por dispersão de energia (EDAX por suas siglas em inglês) e Difração de Raios X (DRX). Além disso, foi realizada simulação termodinâmica mediante o software comercial Thermo-Calc, com a finalidade de aproximar às condições ótimas a deposição do recobrimento sobre os mencionados aços. Todos os espécimes, sem e com recobrimento de alumínio por CVD-FBR, foram oxidados à temperatura de 700ºC, em uma atmosfera próxima a 100% de vapor d'água por 1000 h. O recobrimento de alumínio evitou a formação de ilhas ou camada de óxidos e diminuiu o ganho de massa dos aços. O aço AISI 304 com recobrimento apresentou uma redução de 25% no ganho de massa em comparação com o mesmo aço sem recobrimento e oxidado nas mesmas condições; os aços AISI 316 e AISI 317 apresentaram perda de massa, devido a que o óxido formado se solta por sua natureza quebradiça
Se han obtenido recubrimientos de aluminio por la técnica de deposición química de vapor por lecho fluidizado (CVD-FBR de sus siglas en inglés), sobre aceros inoxidables austeníticos (AISI 304, AISI 316 y AISI 317), con el propósito de evaluar la resistencia a la oxidación en vapor de agua a 700ºC. Los recubrimientos fueron caracterizados en su morfología/composición y fases cristalinas mediante las técnicas de Microscopía Electrónica de Barrido (MEB), con análisis de rayos X por dispersión de energía (EDAX de sus siglas en ingles) y Difracción de Rayos X (DRX). Además, se realizó simulación termodinámica mediante el software comercial Thermo-Calc, con la finalidad de aproximar a las condiciones óptimas la deposición del recubrimiento sobre los mencionados aceros. Todos los especímenes sin y con recubrimiento de aluminio por CVD-FBR, fueron oxidados a la temperatura de 700ºC, en una atmósfera próxima al 100% de vapor de agua por 1000 h. El recubrimiento de aluminio evitó la formación de islas o costra de óxidos y disminuyó la ganancia de masa de los aceros. El acero AISI 304 con recubrimiento presentó una reducción del 25% en la ganancia de masa en comparación con el mismo acero sin recubrimiento y oxidado en las mismas condiciones; los aceros AISI 316 y AISI 317 presentaron pérdida de masa, debido a que el óxido formado se desprende por su naturaleza quebradiza
Analítica
analitica Rebiun33880792 https://catalogo.rebiun.org/rebiun/record/Rebiun33880792 230421s2014 xx o 000 0 eng d https://dialnet.unirioja.es/servlet/oaiart?codigo=5430594 (Revista) ISSN 0122-5383 S9M oai:dialnet.unirioja.es:ART0000943170 https://dialnet.unirioja.es/oai/OAIHandler 16 DGCNT S9M S9M dc Behavior of aluminum coating by cvd-fbr in steam oxidation at 700c electronic resource] 2014 application/pdf Open access content. Open access content star Aluminum coatings have been obtained using the Chemical Vapor Deposition of Fluidized Bed Reactor technique (CVD-FBR), on austenitic stainless steels (AISI 304, AISI 316 and AISI 317), in order to evaluate resistance to steam oxidation at 700ºC. The coatings were characterized in their morphology/composition and crystalline phases using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Analysis (EDAX) and X-ray Diffraction (XRD). In addition, thermodynamic simulation was performed using Thermo-Calc software to make the deposition of the coating on said steels similar to optimal conditions. All specimens -with and without aluminum coating by CVD-FBR- were oxidized at 700ºC, in a steam atmosphere of nearly 100% for 1000 h. The aluminum coating prevented the formation of oxide islands or crust, and reduced steel mass gain. Coated AISI steel showed a 25% reduction in mass gain compared to the same steel uncoated and oxidized under the same conditions. AISI 316 and AISI 317 steels underwent loss of mass because the brittle oxide that was formed came loose Foram obtidos recobrimentos de alumínio pela técnica de deposição química de vapor por leito fluidizado (CVD-FBR por suas siglas em inglês), sobre aços inoxidáveis austeníticos (AISI 304, AISI 316 e AISI 317), com o propósito de avaliar a resistência à oxidação em vapor d'água a 700ºC. Os recobrimentos foram caracterizados em sua morfologia/composição e fases cristalinas mediante as técnicas de Microscopia Eletrônica de Varredura (MEB), com análise de raios X por dispersão de energia (EDAX por suas siglas em inglês) e Difração de Raios X (DRX). Além disso, foi realizada simulação termodinâmica mediante o software comercial Thermo-Calc, com a finalidade de aproximar às condições ótimas a deposição do recobrimento sobre os mencionados aços. Todos os espécimes, sem e com recobrimento de alumínio por CVD-FBR, foram oxidados à temperatura de 700ºC, em uma atmosfera próxima a 100% de vapor d'água por 1000 h. O recobrimento de alumínio evitou a formação de ilhas ou camada de óxidos e diminuiu o ganho de massa dos aços. O aço AISI 304 com recobrimento apresentou uma redução de 25% no ganho de massa em comparação com o mesmo aço sem recobrimento e oxidado nas mesmas condições; os aços AISI 316 e AISI 317 apresentaram perda de massa, devido a que o óxido formado se solta por sua natureza quebradiça Se han obtenido recubrimientos de aluminio por la técnica de deposición química de vapor por lecho fluidizado (CVD-FBR de sus siglas en inglés), sobre aceros inoxidables austeníticos (AISI 304, AISI 316 y AISI 317), con el propósito de evaluar la resistencia a la oxidación en vapor de agua a 700ºC. Los recubrimientos fueron caracterizados en su morfología/composición y fases cristalinas mediante las técnicas de Microscopía Electrónica de Barrido (MEB), con análisis de rayos X por dispersión de energía (EDAX de sus siglas en ingles) y Difracción de Rayos X (DRX). Además, se realizó simulación termodinámica mediante el software comercial Thermo-Calc, con la finalidad de aproximar a las condiciones óptimas la deposición del recubrimiento sobre los mencionados aceros. Todos los especímenes sin y con recubrimiento de aluminio por CVD-FBR, fueron oxidados a la temperatura de 700ºC, en una atmósfera próxima al 100% de vapor de agua por 1000 h. El recubrimiento de aluminio evitó la formación de islas o costra de óxidos y disminuyó la ganancia de masa de los aceros. El acero AISI 304 con recubrimiento presentó una reducción del 25% en la ganancia de masa en comparación con el mismo acero sin recubrimiento y oxidado en las mismas condiciones; los aceros AISI 316 y AISI 317 presentaron pérdida de masa, debido a que el óxido formado se desprende por su naturaleza quebradiza LICENCIA DE USO: Los documentos a texto completo incluidos en Dialnet son de acceso libre y propiedad de sus autores y/o editores. Por tanto, cualquier acto de reproducción, distribución, comunicación pública y/o transformación total o parcial requiere el consentimiento expreso y escrito de aquéllos. Cualquier enlace al texto completo de estos documentos deberá hacerse a través de la URL oficial de éstos en Dialnet. Más información: https://dialnet.unirioja.es/info/derechosOAI | INTELLECTUAL PROPERTY RIGHTS STATEMENT: Full text documents hosted by Dialnet are protected by copyright and/or related rights. This digital object is accessible without charge, but its use is subject to the licensing conditions set by its authors or editors. Unless expressly stated otherwise in the licensing conditions, you are free to linking, browsing, printing and making a copy for your own personal purposes. All other acts of reproduction and communication to the public are subject to the licensing conditions expressed by editors and authors and require consent from them. Any link to this document should be made using its official URL in Dialnet. More info: https://dialnet.unirioja.es/info/derechosOAI English Aluminum coatings Chemical Vapor Deposition in Fluidized Bed Reactors (CVD-FBR) High-temperature corrosion Steam oxidation Austenitic stainless steels Recubrimientos de aluminio Deposición química por lecho fluidizado (CVD-FBR) Corrosión a alta temperatura Oxidación en vapor de agua Aceros inoxidables austeníticos Recobrimentos de alumínio Deposição química por letio fluidizado (CVD-FBR) Corrosão a alta temperatura Oxidação em vapor d'água Aços inoxidáveis austeníticos text (article) Marulanda Arévalo, José Luddey. cre Pérez Trujillo, Francisco Javier. cre Castañeda Quintana, Saul. cre CT&F - Ciencia, tecnología y futuro, ISSN 0122-5383, Vol. 5, Nº. 4, 2014, pags. 75-84 CT&F - Ciencia, tecnología y futuro, ISSN 0122-5383, Vol. 5, Nº. 4, 2014, pags. 75-84 CT&F - Ciencia, tecnología y futuro, ISSN 0122-5383, Vol. 5, Nº. 4, 2014, pags. 75-84