Descripción del título
Características mecánicas y...
The mechanical and acoustic properties of four commonly used wood species, including Populus tomentosa (Poplar), Swietenia mahagoni (Mahogany), Fagus orientalis (Beech), and Fraxinus excelsior (Ash) wood were investigated through using three-point bending and notched bending tests synchronizing with power spectrum analysis method and fractal dimension theory. The results showed that the bending modulus of elasticity and modulus of rapture changed in the same trend with the order ranging from high to low was ash, beech, poplar, and mahogany, successively. The brittle fracture occurred in mahogany samples and duc-tile fracture raised in the other three wood species. Positive proportional correlation was observed between maximum acoustic pressure and fractal dimension of power spectrum regardless of seeing four wood species as independent or population samples. The failure modes can be identified by amplitude-frequency curve and fractal dimension of power spectrum with following laws: the peak value in amplitude-frequency curve and fractal dimension of power spectrum were relatively higher when a single crack developed at latewood; for crack developed at earlywood, only one peak was observed in power amplitude-frequency curves, and the corresponding fractal dimension of power spectrum was smaller than the that of latewood; in case of failure modes with two cracks developed at earlywood, there are two peaks in amplitude-frequency curve and the frac-tal dimension of power spectrum was between those of single crack developed at earlywood and latewood. The vibrational properties of the four wood species can be characterized through using power spectrum analysis method and notched bending test method can be used to distinguish the failure modes of samples
Las propiedades mecánicas y acústicas de cuatro especies de madera de uso común, incluido el álamo ( Populus tomentosa ), la caoba ( Swietenia mahagoni ), el haya ( Fagus orientalis ) y el fresno ( Fraxinus excelsior ) la madera se investigó mediante pruebas de flexión de tres puntos y de flexión con muescas sincronizadas con el método de análisis del espectro de potencia y la teoría de la dimensión fractal. Los resultados mostraron que el módulo de elasticidad de flexión y el módulo de éxtasis cambiaron en la misma tendencia con el orden de mayor a menor en fresno, haya, álamo y caoba, sucesivamente. La fractura frágil ocurrió en muestras de caoba y la fractura dúctil surgió en las otras tres especies de madera. Se observó una correlación proporcional positiva entre la presión acústica máxima y la dimensión fractal del espectro de potencia independientemente de considerar cuatro especies de madera como muestras independientes o de población. Los modos de falla se pueden identificar mediante la curva amplitud-frecuencia y la dimensión fractal del espectro de potencia con las siguientes leyes: el valor máximo en la curva de amplitud-frecuencia y la dimensión fractal del espectro de potencia fueron relativamente más altos cuando se desarrolló una sola grieta en la madera tardía; para las grietas desarrolladas en la madera temprana, solo se observó un pico en las curvas de amplitud-frecuencia de potencia, y la dimensión fractal correspondiente del espectro de potencia fue más pequeña que la de la madera tardía; en el caso de modos de falla con dos grietas desarrolladas en madera temprana, hay dos picos en la curva de amplitud-frecuencia y la dimensión fractal del espectro de potencia estuvo entre las de una sola grieta desarrollada en madera temprana y madera tardía. Las propiedades vibratorias de las cuatro especies de madera se pueden caracterizar mediante el uso del método de análisis del espectro de potencia y el método de prueba de flexión con muescas se puede u
Analítica
analitica Rebiun34998151 https://catalogo.rebiun.org/rebiun/record/Rebiun34998151 240121s2023 xx o 000 0 spa d https://dialnet.unirioja.es/servlet/oaiart?codigo=9125525 (Revista) ISSN 0717-3644 (Revista) ISSN 0718-221X S9M oai:dialnet.unirioja.es:ART0001629324 https://dialnet.unirioja.es/oai/OAIHandler 15 DGCNT S9M S9M dc Características mecánicas y acústicas de cuatro especies de madera sometidas a cargas de flexión electronic resource] 2023 application/pdf Open access content. Open access content star The mechanical and acoustic properties of four commonly used wood species, including Populus tomentosa (Poplar), Swietenia mahagoni (Mahogany), Fagus orientalis (Beech), and Fraxinus excelsior (Ash) wood were investigated through using three-point bending and notched bending tests synchronizing with power spectrum analysis method and fractal dimension theory. The results showed that the bending modulus of elasticity and modulus of rapture changed in the same trend with the order ranging from high to low was ash, beech, poplar, and mahogany, successively. The brittle fracture occurred in mahogany samples and duc-tile fracture raised in the other three wood species. Positive proportional correlation was observed between maximum acoustic pressure and fractal dimension of power spectrum regardless of seeing four wood species as independent or population samples. The failure modes can be identified by amplitude-frequency curve and fractal dimension of power spectrum with following laws: the peak value in amplitude-frequency curve and fractal dimension of power spectrum were relatively higher when a single crack developed at latewood; for crack developed at earlywood, only one peak was observed in power amplitude-frequency curves, and the corresponding fractal dimension of power spectrum was smaller than the that of latewood; in case of failure modes with two cracks developed at earlywood, there are two peaks in amplitude-frequency curve and the frac-tal dimension of power spectrum was between those of single crack developed at earlywood and latewood. The vibrational properties of the four wood species can be characterized through using power spectrum analysis method and notched bending test method can be used to distinguish the failure modes of samples Las propiedades mecánicas y acústicas de cuatro especies de madera de uso común, incluido el álamo ( Populus tomentosa ), la caoba ( Swietenia mahagoni ), el haya ( Fagus orientalis ) y el fresno ( Fraxinus excelsior ) la madera se investigó mediante pruebas de flexión de tres puntos y de flexión con muescas sincronizadas con el método de análisis del espectro de potencia y la teoría de la dimensión fractal. Los resultados mostraron que el módulo de elasticidad de flexión y el módulo de éxtasis cambiaron en la misma tendencia con el orden de mayor a menor en fresno, haya, álamo y caoba, sucesivamente. La fractura frágil ocurrió en muestras de caoba y la fractura dúctil surgió en las otras tres especies de madera. Se observó una correlación proporcional positiva entre la presión acústica máxima y la dimensión fractal del espectro de potencia independientemente de considerar cuatro especies de madera como muestras independientes o de población. Los modos de falla se pueden identificar mediante la curva amplitud-frecuencia y la dimensión fractal del espectro de potencia con las siguientes leyes: el valor máximo en la curva de amplitud-frecuencia y la dimensión fractal del espectro de potencia fueron relativamente más altos cuando se desarrolló una sola grieta en la madera tardía; para las grietas desarrolladas en la madera temprana, solo se observó un pico en las curvas de amplitud-frecuencia de potencia, y la dimensión fractal correspondiente del espectro de potencia fue más pequeña que la de la madera tardía; en el caso de modos de falla con dos grietas desarrolladas en madera temprana, hay dos picos en la curva de amplitud-frecuencia y la dimensión fractal del espectro de potencia estuvo entre las de una sola grieta desarrollada en madera temprana y madera tardía. Las propiedades vibratorias de las cuatro especies de madera se pueden caracterizar mediante el uso del método de análisis del espectro de potencia y el método de prueba de flexión con muescas se puede u LICENCIA DE USO: Los documentos a texto completo incluidos en Dialnet son de acceso libre y propiedad de sus autores y/o editores. Por tanto, cualquier acto de reproducción, distribución, comunicación pública y/o transformación total o parcial requiere el consentimiento expreso y escrito de aquéllos. Cualquier enlace al texto completo de estos documentos deberá hacerse a través de la URL oficial de éstos en Dialnet. Más información: https://dialnet.unirioja.es/info/derechosOAI | INTELLECTUAL PROPERTY RIGHTS STATEMENT: Full text documents hosted by Dialnet are protected by copyright and/or related rights. This digital object is accessible without charge, but its use is subject to the licensing conditions set by its authors or editors. Unless expressly stated otherwise in the licensing conditions, you are free to linking, browsing, printing and making a copy for your own personal purposes. All other acts of reproduction and communication to the public are subject to the licensing conditions expressed by editors and authors and require consent from them. Any link to this document should be made using its official URL in Dialnet. More info: https://dialnet.unirioja.es/info/derechosOAI Spanish Dimensión fractal propiedades mecánicas flexión con muesca característica vibratoria especies de madera Fractal dimension mechanical properties notched bending vibrational characteristic wood species text (article) Hu, Wengang. cre Yu, Runzhong. cre Maderas: Ciencia y tecnología, ISSN 0718-221X, Vol. 25, Nº. 1, 2023 Maderas: Ciencia y tecnología, ISSN 0718-221X, Vol. 25, Nº. 1, 2023 Maderas: Ciencia y tecnología, ISSN 0718-221X, Vol. 25, Nº. 1, 2023