Descripción del título
Effect of Alternative Self-...
Objective: This study evaluated the effects of alternative self-etch application modes on resin-dentin microtensile bond strength (µTBS) of three commercially available "no wait" concept universal adhesives. Materials and methods: In this study extracted impacted non-carious human third molars were used. The flat surfaces were prepared in mid-coronal dentin and prepared with a 600-grit SiC paper. The three universal adhesives that were used are as follows: Clearfil Universal Bond Quick (CUQ, Kuraray Noritake, Japan), G-Premio Bond (GPB, GC Corp, Japan), and a self-curing universal adhesive "Tokuyama Universal Bond" (TUB; Tokuyama Dental, Japan). The following three different application procedures were used for the dentin surfaces: the adhesives were applied and immediately subjected to air-dry; the adhesives were applied followed by a 10-second wait; or the adhesives were rubbed for 10 seconds. Then composite resin was applied to the dentin surface and light cured. After storage in 37C distilled water for 24 h, all the bonded teeth were cut into 1mmp2(B sections using a low-speed diamond saw (Micracut 125 Low Speed Precision Cutter, Metkon, Bursa, Turkey) under running water (n=15). The sections were subjected to a tensile force at a crosshead speed of 1mm/min in a testing apparatus (Microtensile Tester, Bisco, IL, USA) and µTBS values were measured. Data were analyzed using the Kruskal-Wallis test and Mann-Whitney U test. Failure modes were analyzed under a stereomicroscope. Results: Prolonged application time significantly affected the µTBS (p<0.005). A significant increase of µTBS on active application was observed for CUQ and GPB. The TUB with an active application had a significantly lower µTBS value compared with the other adhesives. Conclusions: Prolonged application time caused significant improvement of bond strength in all adhesives. The active application is effective at increasing the dentin bond strength except for TUB
Objetivo: Este estudio evaluó los efectos de los modos alternativos de aplicación de adhesivos de autograbado en la resistencia de la unión microtensil entre resina y dentina (µTBS) de tres adhesivos universales de concepto "no espera" disponibles en el mercado. Materiales y métodos: En este estudio se utilizaron terceros molares humanos impactados que fueron extraídos. Las superficies planas se prepararon en la dentina coronal media y se prepararon con un papel SiC de 600 granos. Los tres adhesivos universales que se utilizaron son los siguientes: Clearfil Universal Quick Bond (CUQ, Kuraray Noritake, Japón), G-Premio Bond (GPB, GC Corp, Japón), y un adhesivo universal autopolimerizable "Tokuyama Universal Bond" (TUB; Tokuyama Dental, Japón). Se utilizaron los tres procedimientos de aplicación siguientes para las superficies dentinarias: se aplicaron los adhesivos y se sometieron inmediatamente a un secado al aire; se aplicaron los adhesivos y se esperó 10 segundos; o se frotaron los adhesivos durante 10 segundos. Luego se aplicó resina compuesta a la superficie dentinaria y se fotopolimerizó. Después de su almacenamiento en agua destilada a 37C durante 24 h, todos los dientes unidos se cortaron en secciones de 1mmp2(B utilizando una sierra de diamante de baja velocidad (Micracut 125 Low Speed Precision Cutter, Metkon, Bursa, Turquía) bajo agua corriente (n=15). Las secciones fueron sometidas a una fuerza de tracción a una velocidad de cruceta de 1mm/min en una máquina de prueba universal (Microtensile Tester, Bisco, IL, USA) y se midieron los valores de µTBS. Los datos fueron analizados utilizando la prueba de Kruskal-Wallis y la prueba U de Mann-Whitney. Los modos de falla fueron analizados bajo un estereomicroscopio. Resultados: El prolongado tiempo de aplicación afectó significativamente a los µTBS (p<0,005). Se observó un aumento significativo de µTBS en la aplicación activa para el CUQ y el GPB. El TUB con una aplicación activa tuvo un valor de µTBS significativ
Analítica
analitica Rebiun35078171 https://catalogo.rebiun.org/rebiun/record/Rebiun35078171 240128s2021 xx o 000 0 eng d https://dialnet.unirioja.es/servlet/oaiart?codigo=8996192 (Revista) ISSN 2215-3411 (Revista) ISSN 1659-1046 S9M oai:dialnet.unirioja.es:ART0001607091 https://dialnet.unirioja.es/oai/OAIHandler 14 DGCNT S9M S9M dc Effect of Alternative Self-Etch Applications on Dentin Bond Strength of "No Wait Concept" Universal Adhesives electronic resource] 2021 application/pdf Open access content. Open access content star Objective: This study evaluated the effects of alternative self-etch application modes on resin-dentin microtensile bond strength (µTBS) of three commercially available "no wait" concept universal adhesives. Materials and methods: In this study extracted impacted non-carious human third molars were used. The flat surfaces were prepared in mid-coronal dentin and prepared with a 600-grit SiC paper. The three universal adhesives that were used are as follows: Clearfil Universal Bond Quick (CUQ, Kuraray Noritake, Japan), G-Premio Bond (GPB, GC Corp, Japan), and a self-curing universal adhesive "Tokuyama Universal Bond" (TUB; Tokuyama Dental, Japan). The following three different application procedures were used for the dentin surfaces: the adhesives were applied and immediately subjected to air-dry; the adhesives were applied followed by a 10-second wait; or the adhesives were rubbed for 10 seconds. Then composite resin was applied to the dentin surface and light cured. After storage in 37C distilled water for 24 h, all the bonded teeth were cut into 1mmp2(B sections using a low-speed diamond saw (Micracut 125 Low Speed Precision Cutter, Metkon, Bursa, Turkey) under running water (n=15). The sections were subjected to a tensile force at a crosshead speed of 1mm/min in a testing apparatus (Microtensile Tester, Bisco, IL, USA) and µTBS values were measured. Data were analyzed using the Kruskal-Wallis test and Mann-Whitney U test. Failure modes were analyzed under a stereomicroscope. Results: Prolonged application time significantly affected the µTBS (p<0.005). A significant increase of µTBS on active application was observed for CUQ and GPB. The TUB with an active application had a significantly lower µTBS value compared with the other adhesives. Conclusions: Prolonged application time caused significant improvement of bond strength in all adhesives. The active application is effective at increasing the dentin bond strength except for TUB Objetivo: Este estudio evaluó los efectos de los modos alternativos de aplicación de adhesivos de autograbado en la resistencia de la unión microtensil entre resina y dentina (µTBS) de tres adhesivos universales de concepto "no espera" disponibles en el mercado. Materiales y métodos: En este estudio se utilizaron terceros molares humanos impactados que fueron extraídos. Las superficies planas se prepararon en la dentina coronal media y se prepararon con un papel SiC de 600 granos. Los tres adhesivos universales que se utilizaron son los siguientes: Clearfil Universal Quick Bond (CUQ, Kuraray Noritake, Japón), G-Premio Bond (GPB, GC Corp, Japón), y un adhesivo universal autopolimerizable "Tokuyama Universal Bond" (TUB; Tokuyama Dental, Japón). Se utilizaron los tres procedimientos de aplicación siguientes para las superficies dentinarias: se aplicaron los adhesivos y se sometieron inmediatamente a un secado al aire; se aplicaron los adhesivos y se esperó 10 segundos; o se frotaron los adhesivos durante 10 segundos. Luego se aplicó resina compuesta a la superficie dentinaria y se fotopolimerizó. Después de su almacenamiento en agua destilada a 37C durante 24 h, todos los dientes unidos se cortaron en secciones de 1mmp2(B utilizando una sierra de diamante de baja velocidad (Micracut 125 Low Speed Precision Cutter, Metkon, Bursa, Turquía) bajo agua corriente (n=15). Las secciones fueron sometidas a una fuerza de tracción a una velocidad de cruceta de 1mm/min en una máquina de prueba universal (Microtensile Tester, Bisco, IL, USA) y se midieron los valores de µTBS. Los datos fueron analizados utilizando la prueba de Kruskal-Wallis y la prueba U de Mann-Whitney. Los modos de falla fueron analizados bajo un estereomicroscopio. Resultados: El prolongado tiempo de aplicación afectó significativamente a los µTBS (p<0,005). Se observó un aumento significativo de µTBS en la aplicación activa para el CUQ y el GPB. El TUB con una aplicación activa tuvo un valor de µTBS significativ LICENCIA DE USO: Los documentos a texto completo incluidos en Dialnet son de acceso libre y propiedad de sus autores y/o editores. Por tanto, cualquier acto de reproducción, distribución, comunicación pública y/o transformación total o parcial requiere el consentimiento expreso y escrito de aquéllos. Cualquier enlace al texto completo de estos documentos deberá hacerse a través de la URL oficial de éstos en Dialnet. Más información: https://dialnet.unirioja.es/info/derechosOAI | INTELLECTUAL PROPERTY RIGHTS STATEMENT: Full text documents hosted by Dialnet are protected by copyright and/or related rights. This digital object is accessible without charge, but its use is subject to the licensing conditions set by its authors or editors. Unless expressly stated otherwise in the licensing conditions, you are free to linking, browsing, printing and making a copy for your own personal purposes. All other acts of reproduction and communication to the public are subject to the licensing conditions expressed by editors and authors and require consent from them. Any link to this document should be made using its official URL in Dialnet. More info: https://dialnet.unirioja.es/info/derechosOAI English Universal adhesives Dentin bond strength Application time Application mode Microtensile Adhesivos universales Resistencia adhesiva a dentina Tiempo de aplicación Modo de aplicación Microtensil text (article) Serin Kalay, Tugba. cre Zaim, Beyza. cre Odovtos: International Journal of Dental Sciences, ISSN 1659-1046, 2021, pags. 282-290 Odovtos: International Journal of Dental Sciences, ISSN 1659-1046, 2021, pags. 282-290 Odovtos: International Journal of Dental Sciences, ISSN 1659-1046, 2021, pags. 282-290